A computer simulation study of point defects in diopside and the self-diffusion of Mg and Ca by a vacancy mechanism

University of Manchester, Materials Science Centre, Manchester, United Kingdom

Computer simulation techniques have been used to investigate defect formation and the diffusion of Ca and Mg in diopside. It was found that isolated, non-interacting CaO and MgO Schottky defects had the lowest formation energies (3.66 and 3.97 eV respectively); oxygen Frenkel defects are the most favourable oxygen defects (formation energies 3.93 eV). Magnesium and calcium self-diffusion in the c-direction of diopside is easiest by a vacancy mechanism involving either direct jumps along the c-direction, or double jumps in the b-c plane. In the extrinsic regime, diffusion activation energies for Mg are predicted to be 9.82 eV (direct route) and 1.97 eV (double jump route); for Ca diffusion, activation energies are predicted to be 6.62 eV (direct route) and 5.63 eV (double jump route). If additional vacancies (oxygen or magnesium) are present in the vicinity of the diffusion path, Ca migration energies fall to 1.97-2.59 eV. At elevated temperatures in the intrinsic regime, diffusion activation energies of > or =5.95 eV are predicted for Mg self-diffusion and 9.29-10.28 eV for Ca self-diffusion. The values for Ca diffusion are comparable with published experimental data. It is inferred that a divacancy mechanism may operate in diopside crystals.

This record provided courtesy of AGI/GeoRef.

This article has been cited by other articles:

				A. DIMANOV and V. SAUTTER "Average" interdiffusion of (Fe,Mn)-Mg in natural diopside European Journal of Mineralogy, August 1, 2000; 12(4): 749 - 760. [Abstract] [Full Text] [PDF]